Chemical strengthening of glass

ABSTRACT

Disclosed are improved glass compositions of the SiO2-Na2O-Al2O3 -ZrO2 system for use in chemical strengthening. The improvement of the invention resides in proportioning the components so as to provide better melting glass compositions with lower liquidus temperatures and greater working ranges than normally associated with such systems. Such glasses are better suited for forming by the updraw or float methods.

RELATED APPLICATION

This application is a continuation-in-part of application Serial No. 432,006, filed January 9, 1974, now abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to glass compositions suitable for strengthening by ion exchange and particularly relates to the strengthening of SiO₂ --Na₂ O--Al₂ O₃ --ZrO₂ glasses by potassium ion exchange.

2. Brief description of the Prior Art

U.S. Pat. Nos. 3,485,702 and 3,752,729, both to Mochel, deal with an improved glass composition of the SiO₂ --ZrO₂ --Al₂ O₃ --alkali metal oxide systems for chemical strengthening. These references disclose that the incorporation of 5 to 25 percent, preferably 10 to 25 percent by weight of ZrO₂ in the glass composition results in deep ion exchange penetrations with resultantly high compressive stresses in relatively short periods of time. Unfortunately, these high ZrO₂ containing glasses are not compatible with conventional float and updraw forming methods because of high melting and forming temperatures and unfavorable liquidus temperature-viscosity relationships. U.S. Pat. No. 3,772,135 to Hara et al. discloses glass compositions for chemical strengthening that represent some improvement in temperature-viscosity relationships, but still exhibit undesirably high melting temperatures, and disadvantageously limit the ZrO₂ content to low levels or eliminate it completely.

The liquidus is defined as the temperature at which devitrification or uncontrolled crystallization of the glass first appears as the temperature is lowered. At temperatures slightly below the liquidus, devitrification occurs, sometimes at a relatively rapid rate, and if uncontrolled could ruin the flat glass sheets, severely curtailing production yields. Somewhat related to liquidus and a problem of devitrificaton is the working range of the glass. The working range is defined for the purposes of this invention as the temperature interval between the glass-forming temperature which is usually taken as the glass temperature when the log of the viscosity of the glass is equal to 4 and the liquidus temperature. Melting and forming temperatures are defined for the purposes of this invention as the temperature at which the viscosity of the glass is equal to about 100 poises and 10,000 poises, respectively.

In flat glass manufacturing, it is desirable for a glass to have low melting and forming temperatures to enable easy working of the glass, to conserve fuel and to prevent excessive thermal deterioration of the glass melting and forming equipment. Further, in flat glass manufacturing, particularly by the float and the updraw process, it is desirable that the glass have a low liquidus temperature and a wide working range. A low liquidus temperature insures against devitrification in cold spots of the furnace and a wide working range insures against devitrification. In the glass forming area of the furnace. In the case of manufacturing glass by the updraw process such as the Pittsburgh Process by liquidus temperature of the glass is about 1840° F. and the working range of the glass is about 70° F. Commercial float glass has a liquidus temperature of about 1830° F. and a working range of about 45° F.

ZrO₂ has a pronounced effect on the liquidus temperature and the working range in the family of glasses disclosed in the above-mentioned Mochel patents. With ZrO₂ concentrations above about 51/4 percent, liquidus temperatures begin to increase quite rapidly with increasing ZrO₂. With ZrO₂ concentrations above 51/2 percent by weight, a serious problem develops with respect to float or updraw forming. With these particular glasses, a narrow working range, and in many instances a negative working range, is established, that is, the liquidus temperature is higher than glass-forming temperature and devitrification occurs rather quickly. This could have disastrous effects if such glasses were formed on a commercial scale by the updraw or float methods. In addition, many of the glasses disclosed in the above-mentioned patents have high melting and forming temperatures making them undesirable for commercial flat glass manufacturing.

It is apparent from the above that it would be desirable to provide a family of glass compositions of the SiO₂ --Na₂ O--AL₂ O₃ --ZrO₂ system for use in chemical strengthening which would be more suitable for forming by the updraw and float processes than those SiO₂ --Na₂ O--Al₂ O₃ --ZrO₂ systems disclosed in the prior art. More particularly, it would be desirable to provide a family of glass compositions for ion exchange which have lower melting and forming temperatures and a wider working range than those glass compositions of the SiO₂ --Na₂ O--Al₂ O₃ --ZrO₂ systems disclosed in the prior art for ion exchange.

Besides the references mentioned above, other relevant prior art consists of U.S. Pat. Nos. 3,790,430 to Mochel; 3,498,773 to Grubb et al.; 3,524,737 to Doyle et al.; 3,433,611 to Saunders et al.; 3,416,936 to Sproul, Jr.; 2,252,466 to Hanlein; 3,499,776 to Baak et al.; 2,877,124 to Welsch; 2,978,341 to Bastian et al.; 3,357,876 to Rinehart and British Pat. No. 1,115,972.

SUMMARY OF THE INVENTION

In accordance with this invention, there is provided an improved method for strengthening an alkali metal oxide aluminosilicate glass article in which the alkali metal ions in the surface of the glass article are replaced by larger monovalent metal ions. The improved method is carried out by bringing the surface of the glass article into contact with the source of the larger monovalent metal ions by retaining the glass at an elevated temperature, usually around the glass strain point, to place a compression layer in a surface of the glass article. The improvement of the invention comprises forming the article to be strengthened from an alkali metal oxide-zirconia-aluminosilicate glass consisting essentially of by weight on the oxide basis of about:

    ______________________________________                                                     Percent by Weight                                                  Component     Broad Range  Preferred Range                                     ______________________________________                                         SiO.sub.2     50-58        52-57                                               Na.sub.2 O     8-23        10-19                                               K.sub.2 O      0-15         0-10                                               Na.sub.2 O + K.sub.2 O                                                                       13-25        17-23                                               Al.sub.2 O.sub.3                                                                              7-17         9-13                                               ZrO.sub.2      1-4.5        2-4.5                                              Al.sub.2 O.sub.3 + ZrO.sub.2                                                                 10-21        12-17                                               CaO            0-10        0                                                   MgO            0-6.5       4-6                                                 CaO + MgO       2.5-10     4-6                                                 TiO.sub.2     0-7          1-6                                                 TiO.sub.2 + (MgO + CaO)                                                                       4-14         5-12                                               ______________________________________                                    

When the glass components are maintained within the above prescribed ranges, the glasses have low melting and forming temperatures and have lower liquidus temperatures and greater working ranges than comparable glass compositions containing greater than 5 percent by weight ZrO₂. In fact, with many of the glass compositions of the present invention, devitrification generally occurs so slowly that it is difficult to detect any evidence of devitrification regardless of temperature. At the same time, the glass compositions of the present invention exhibit desirable ion exchange characteristics for purposes of chemical strengthening.

BRIEF DESCRIPTION OF THE DRAWING

The FIGURE is a graph of viscosity versus temperature plots for various glasses of the invention and glasses of the prior art.

DETAILED DESCRIPTION EXAMPLES 1 - 2

The preferred embodiments of the invention employ glasses having the following calculated glass compositions which can be made by conventional melting and forming techniques.

    ______________________________________                                                    Percent by Weight on the Oxide Basis                                Component    Example 1     Example 2                                           ______________________________________                                         SiO.sub.2    56.0          54.5                                                Na.sub.2 O   18.0          18.0                                                Al.sub.2 O.sub.3                                                                            12.0          10.0                                                MgO          4.5           5.0                                                 K.sub.2 O    3.0           3.0                                                 ZrO.sub.2    4.5           4.5                                                 TiO.sub.2    2.0           5.0                                                 ______________________________________                                    

The glass of Example 2 is a better melting glass, i.e., melts at lower temperatures and has a lower viscosity versus temperature curve, than the glass of Example 1. However, the glass of Example 1 has better optical properties, i.e., is less colored and has slightly better radiant energy transmitting properties.

The glasses of the present invention such as set forth above in the preferred embodiments, have extremely good melting and forming properties, being more akin to commercial sheet and float glass than to an ion exchange glass. The FIGURE compares the viscosity-temperature relation of the above glasses with similar relations for commercial sheet glass sold under the trademark PENNVERNON (registered trademark of PPG Industries, Inc.), commercial float glass, for a commercially available ion exchange glass, and for glasses numbered 1, 2, 3 and 10 in Table I of U.S. Pat. 3,485,702, in the viscosity range of 10².0 to 10⁵.0 poises. The calculated composition of PENNVERNON sheet glass is as follows: SiO₂, 73 percent; Na₂ O, 13.3 percent; CaO, 8.2 percent; MgO, 3.7 percent; Al₂ O₃ , 1.2 percent; Fe₂ O₃, 0.1 percent; K₂ O, 0.2 percent; SO₃, 0.2 percent. The commercial float glass had the following actual composition: 73.06 percent SiO₂, 13.64 percent Na₂ O, 0.03 percent K₂ O, 8.86 percent CaO, 3.86 percent MgO, 0.12 percent Al₂ O₃, 0.30 percent SO₃, and 0.13 percent Fe₂ O₃. The actual composition of the commercially available ion exchange glass is as follows: 61.98 percent SiO₂, 13.08 percent Na₂ O, 3.27 percent K₂ O, 3.21 percent MgO, 17.56 percent Al₂ O₃, 0.064 percent Fe₂ O₃, 0.64 percent TiO₂, 0.04 percent Cl⁻, 0.14 percent CaO, 0.07 percent As₂ O₅, and 0.04 percent SO₃. The calculated compositions for the glasses numbered 1, 2, 3 and 10 in Table I of U.S. Pat. No. 3,485,702 are as follows:

    ______________________________________                                                Percent by Weight                                                       Component                                                                               1         2         3       10                                        ______________________________________                                         SiO.sub.2                                                                               66        60        59      52                                        Al.sub.2 O.sub.3                                                                        10        10        10      10                                        ZrO.sub.2                                                                                5        11        12      15                                        Na.sub.2 O                                                                              16        16        16      16                                        K.sub.2 O                                                                                3         3         3       7                                        ______________________________________                                    

U.s. pat. No. 3,772,135 (Hara et al.) discloses only one specific example of a ZrO₂ -containing glass (Example 5), which has the following composition by weight: 62% SiO₂, 10% Al₂ O₃, 1% ZrO₂, 1% TiO₂, 9% Na₂ O, 9% K₂ O, 4% MgO, and 4% ZnO.

The tremendous melting advantage of the glasses of the present invention such as specified above in Examples 1 and 2 over the commercially available ion exchange glass and the ion exchange glass of the prior art is obvious. The melting temperatures or the temperatures corresponding to 100 poises (log₁₀ of the viscosity in poises is equal to 2.0) are as follows:

    ______________________________________                                                            Temperature at viscosity                                    Glass              of 100 poises ° F.                                   ______________________________________                                         Example 1            2700                                                      Example 2            2575                                                      Commercial Sheet Glass                                                                              2705                                                      Commercial Float Glass                                                                              2622                                                      Commercial Ion Exchange                                                        Glass                3185 (estimated value)                                    U.S. Patent 3,485,702 (Mochel)                                                 Example 1            3022                                                      Example 2            2955                                                      Example 3            2953                                                      Example 10           2788                                                      U.S. Patent 3,772,135 (Hara et al)                                             Example 5            2889                                                      ______________________________________                                    

The glass-forming temperature is conventionally taken as the temperature at a viscosity level of about 10,000 poises (log₁₀ of the viscosity in poises is equal to 4.0). Thus, as indicated by the viscosity curves of FIG. 1, the forming temperature of the glass of Example 1 will be about 75° to 80° F. higher than the drawing temperature for commercial sheet glass and for commercial float glass. The glass of Example 2 had a forming temperature approximately equal to both commercial float and commercial sheet glass. The high temperature viscosity properties of the commercial sheet and float glass and the glasses of Examples 1 and 2 are presented in the table below. These high temperature viscosity properties, unless otherewise indicated, were measured according to the procedure described in "Measurements of Absolute Viscosity by the Use of Concentric Cylinder", H. R. Lillie, J. Amer. Ceram, Soc., 12, No. 8, 505 (1929). See also U.S. Pat. No. 3,056,283 to Tiede.

                                      Table I                                      __________________________________________________________________________                 Temperature ° F.                                            Log of the Viscosity                                                                       Commercial                                                                           Commercial                                                                            Glass of                                                                            Glass of                                                                            Commercial Ion                                                                          U.S. Patent 3,485,702                in Poises Sheet Glass                                                                          Float Glass                                                                           Ex. 1                                                                               Ex. 2                                                                               Exchange Glass                                                                          1   2    3    10                   __________________________________________________________________________     2           2705  2622   2700 2575 3185     3022                                                                               2955 2953 2788                 3           2230  2169   2250 2175 2690     2503                                                                               2517 2522 2409                 4           1920  1873   1980 1900 2305     2151                                                                               2223 2232  215                 Liquidus Temperature                                                           ° F. - procedure                                                        described in J. Soc.                                                           Glass Techn., 24,                                                              101-108 (1940) by                                                              E. Preston  1840  1830   *    *                 1560**                                                                              2025**                                                                              2331**               Working Range ° F.                                                                   30    43    >125 >125               663  207 -174                 __________________________________________________________________________       *Attempts to determine the liquidus temperature and the working ranges o      the glasses of Examples 1 and 2 were not successful. An alternate              procedure, other than the one specified in the above table, was then used      to determine the liquidus temperature and working range. Small platinum        packets are filled with glass crushed in a hardened steel mortar and the       packets positioned in sand along the temperature gradient of a gradient        wound tube furnace. After a soak period of at least 66 hours, the packets      are removed and quenched in water. The contents of each packet are then        examined for the presence of crystals in the following manner. The fused       glass is powdered in an agate mortar and a portion of the powder is place      on a microscope slide, along with a drop or two of oil with an index of        refraction close to that of the glass. The submerged glass particles are       then viewed with a microscope at 100X to 200X between crossed polarizers.      In the absence of crystals the field remains dark. Birefringent crystals       will rotate the plane of polarization of the light coming through the          first polarizer and thus appear as bright areas in the dark field. In the      glasses of Examples 1 and 2, no crystals were detected, thus indicating a      working range of at least 125° F.                                       **Liquidus values reported in U.S. Patent 3,485,702.                     

The following series of tests give an indication of the chemical strengthening propensity of the glasses of Examples 1 and 2 in comparison to the commercially available ion exchange glass as described above.

TEST SPECIMENS

The test specimens used for evaluating strength are of two types: the first type of test specimen is a 2 inch by 2 inch by 0.100 inch ground and polished square. All plates are re-annealed. The second type of test specimen is a nominal 3 millimeter (mm) diameter rod approximately 21/2 inches in length. Melts made in 4 inch diameter platinum crucibles provide glass for the test specimens. A melt consists of 750 grams of the oxide glass, homogenized during melting by about 4 hours of continuous stirring. Rods are drawn directly from the melt. The 2 inch square specimens are made from 1/4 inch cast plates. It is the practice to re-anneal all plates and rods to remove thermal history frozen into the plates or rods when formed.

EXCHANGE TREATMENTS

All exchange treatments take place in molten KNO₃, the times and temperatures of the exchange depend upon the desired combination of compression layer thickness and strength.

SPECIMEN ABRASION

Following ion exchange and prior to testing, all strength samples are given 1 of 3 types of abrasion. The first type of abrasion is referred to as heavy abrasion. By this method of abrasion, a 3/4 inch diameter circular area, centrally located on a 2 inch square specimen, is blasted with 2 cubic centimeters (cc) of 100 grit Al₂ O₃ with an air pressure of 30 psi. This is the type of abrasion used in testing chemically strengthened glass for aircraft applications.

The second type of abrasion is referred to as light abrasion. In the practice of this invention, this type of abrasion is used with 2 inch square specimens for tests that apply to automotive and/or architectural applications. A 1/2 inch diameter circular area, centrally located on a specimen, is abraded with 10 cc of 25-30 grit silicon carbide that falls freely in a normal direction onto the area from a height of 12 inches.

The third type of abrasion is referred to as tumble abrasion. This type of abrasion is applicable to rods. A 16 ounce jar containing 10 rod specimens and 200 cc of 240 grit silicon carbide rotates about its main axis at a speed of about 167 rpm for 30 minutes.

TEST METHODS

Using a Rhiele testing machine, the 2 inch squares are evaluated for modulus of rupture by the method of concentrically loading, with the abraded surface placed in tension. The diameter of the load ring is 3/4 inch. That of the support ring is 11/2 inches. The modulus of rupture (MOR) corrected for both overhang and membrane effects is obtained as a computer solution of the following expression:

    W = 2.160 σ h.sup.2 + 2.325 × 10.sup..sup.-15 σ.sup.3 /h.sup. 2

where W is the load at fracture, σ is the modulus of rupture and h is the glass thickness. The test method for rods employs a 4 point loading configuration with a 11/2 inch support span and a 3/4 inch load span. The modulus of rupture for rods is given by the expression:

    σ = 8WL/π ab.sup.2

where W is the load at fracture, L is the distance between load and support points, a is the large diameter of the rod, b is the small diameter of the rod.

Table II presented immediately below shows the average modulus of rupture for the glass of Examples 1 and 2 given two different exchange treatments, both of which produce compression layers about 7 mils thick. A compression layer of this thickness is believed desirable for most use in aircraft applications. The results are also for samples given a heavy type of abrasion as described above.

                                      Table II                                     __________________________________________________________________________     Abraded MOR of Glasses of Examples 1 and 2                                     and Commercially Available Ion Exchange Glass                                  Glass    Exchange Conditions                                                                        Layer Depth                                                                            Abraded MOR                                       __________________________________________________________________________     Example 1                                                                               24 hours - 950° F. -                                                                7 mils  57,800 psi                                                 KNO.sub.3                                                             Example 2                                                                               "           "       56,800 psi                                        Comm. Ion                                                                               "           8 mils  57,700 psi                                        Exchange Glass                                                                 Example 2                                                                               48 hours - 900° F. -                                                                7 mils  69,400 psi                                                 KNO.sub.3                                                             Comm. Ion                                                                               "           8 mils  59,200 psi                                        Exchange Glass                                                                 Example 1                                                                               96 hours - 850° F. -                                                                7 mils  77,900 psi                                                 KNO.sub.3                                                             Comm. Ion                                                                               "           8 mils  66,200 psi                                        Exchange Glass                                                                 __________________________________________________________________________

With respect to potential aircraft use, it is clear that glasses of Examples 1 and 2 are as applicable as the commercially available ion exchange glass.

The suggested range of flexural strength for automotive windshield glass is 40,000 to 50,000 psi. Table III below shows the specific exchange conditions needed to provide the 2 inch square specimens of the glasses of Example 1 with nominal 2, 3 and 4 mil compression layers and an average strength falling within the suggested range. Tests were conducted with 2 inch by 2 inch by 0.100 inch ground and polished squares and light abrasion was used.

                  Table III                                                        ______________________________________                                         Exchange Conditions for 2, 3 and 4 mil Compression Layers                      On Glass of Example 1                                                          With Modulus of Rupture in the 40,000-50,000 psi Range                         Exchange                                                                       Temperature                                                                              Time       Layer Depth MOR                                           ______________________________________                                         1050° F.                                                                          0.5 hour   2.0 mils    45,200 psi                                    1050° F.                                                                          1.1 hours  2.9 mils    42,300 psi                                    1025° F.                                                                          3.0 hours  4.0 mils    46,500 psi                                    ______________________________________                                    

The strength corresponding to a given compression layer thickness can be increased by carrying out the exchange at lower salt bath temperatures for longer times. Table IV below summarizes the results of modulus of rupture tests using tumble abraded rods of the glasses of Examples 1 and 2 exchanged at different temperatures for a period sufficient to produce 2 mil compression layers.

                                      Table IV                                     __________________________________________________________________________     Modulus of Rupture for Rods of Glasses of Examples 1 and 2                     With 2 mil Compression Layer Produced at Different Temperatures                Glass of Example 1         Glass of Example 2                                  Exchange                   Exchange                                            Treatment   Layer Depth                                                                            MOR    Treatment   Layer Depth                                                                            MOR                             __________________________________________________________________________     4 hours - 900° F. -                                                                 2 mils  88,700 psi                                                                            4 hours - 900° F. -                                                                 2 mils  90,300 psi                      KNO.sub.3                  KNO.sub.3                                           2 hours - 950° F. -                                                                 "       77,200 psi                                                                            2 hours - 950° F. -                                                                 "       80,300 psi                      KNO.sub.3                  KNO.sub.3                                           1 hour - 1000° F. -                                                                 "       66,100 psi                                                                            1 hour - 1000° F. -                                                                 "       69,900 psi                      KNO.sub.3                  KNO.sub.3                                           1/2 hour - 1050° F. -                                                               "       50,700 psi                                                                            1/2 hour - 1050° F. -                                                               "       49,000 psi                      KNO.sub.3                  KNO.sub.3                                           __________________________________________________________________________

By way of comparison, the glass of Example 5 in U.S. Pat. No. 3,772,135 (Hara et al.), after being ion-exchanged in KNO₃ at 1000° F. for 1 hour, was found to have a compression layer depth of 1.8 to 1.9 mils but an abraded rod MOR of only 17,600 psi. When ion-exchanged for 4 hours in KNO₃ at 900° F., Hara's Example 5 glass exhibited an abraded rod MOR of 47,100 psi and a compression layer depth of 2.2 mils.

As has been mentioned, the glasses of the present invention are practically non-devitrifiable which makes them amenable to forming in sheet form by the updraw and float process. In sheet form, the glasses can be used to make chemically tempered glass patio and storm doors. Formerly, strengthened glass patio and storm doors have been thermally tempered.

However, there are a number of advantages associated with chemical tempering over thermal tempering. As the glass becomes thinner, it becomes increasingly more difficult to store sufficient internal energy by the thermal tempering method to produce small particles which are required by the safety codes for storm and patio doors, when fractures occur. On the other hand, with chemical tempering, it becomes easier to develop the necessary internal stress for small fracture particles when the glass becomes thinner, thus satisfying practically all of the safety codes. Also, with thermal tempering, there is a decided tendency for thin glass to distort when heated to temperatures required for thermal tempering. Distortion during chemical tempering is minimal, regardless of glass thickness. However, because of the slow rate of penetration of the strengthening ion and the low level of surface compressive stress produced, it is virtually impossible to generate sufficient internal stress in conventional soda-lime-silica glass by chemical means to satisfy the safety code for tempered storm and patio doors regarding particle size. However, glasses of the present invention can be sufficiently tempered by chemical means to satisfy the tempered glass safety code.

The following table shows the exchange times needed to produce center tension levels of 2100, 2500, 3000 and 4000 millimicrons (mu) per inch for the glass of Examples 1 to 2 of nominal 0.10 inch thickness. The center tension levels are expressed in terms of retardation measured by the graduated quartz wedge technique.

    __________________________________________________________________________     Glass of Example 1          Glass of Example 2                                 Center Tension                                                                          Salt Temperature                                                                         Exchange Time                                                                           Center Tension                                                                          Salt Temperature                                                                         Exchange                        __________________________________________________________________________                                                    Time                            2100 mu/inch                                                                            975° F.                                                                            7.2 hours                                                                              2100 mu/inch                                                                            975° F.                                                                            9.0 hours                      2500 mu/inch                                                                            975° F.                                                                           11.5 hours                                                                              2500 mu/inch                                                                            975° F.                                                                           15.4 hours                      3000 mu/inch                                                                            975° F.                                                                           19.6 hours                                                                              3000 mu/inch                                                                            975° F.                                                                           27.2 hours                      4000 mu/inch                                                                            975° F.                                                                           48.3 hours                                                                              4000 mu/inch                                                                            975° F.                                                                           65.6 hours                      __________________________________________________________________________

It will require shorter exchange times to produce the same stress levels in thinner glass. For example, to produce center tension levels of 2100 to 4000 mu/inch in the above glass of 0.0750 inch thickness will require the following exchange times.

    __________________________________________________________________________     Glass of Example 1          Glass of Example 2                                 Center Tension                                                                          Salt Temperature                                                                         Exchange Time                                                                           Center Tension                                                                          Salt Temperature                                                                         Exchange                        __________________________________________________________________________                                                    Time                            2100 mu/inch                                                                            975° F.                                                                            2.3 hours                                                                              2100 mu/inch                                                                            975° F.                                                                            3.3 hours                      2500 mu/inch                                                                            975° F.                                                                            3.6 hours                                                                              2500 mu/inch                                                                            975° F.                                                                            5.0 hours                      3000 mu/inch                                                                            975° F.                                                                            5.9 hours                                                                              3000 mu/inch                                                                            975° F.                                                                            8.0 hours                      4000 mu/inch                                                                            975° F.                                                                           13.1 hours                                                                              4000 mu/inch                                                                            975° F.                                                                           20.2 hours                      __________________________________________________________________________

The ion strengthened special glasses such as described above are stronger than fully heat tempered soda-lime-silica glass. The modulus of rupture of the above chemically tempered glass is at least two times that of fully heat treated soda-lime-silica glass. On this basis, tempered glass such as described above of 0.090 inch thickness will have the same load bearing strength as 0.125 inch fully heat tempered soda-lime-silica glass. Full temper by thermal quench is presently limited to glasses of 0.125 inch and above for soda-lime-silica glass. Thus, with the special glasses of the present invention and chemical tempering, it is possible to reduce the lower thickness limit for fully tempered glass by 29 percent or more without jeopardizing safety or load bearing strength.

The glass compositions referred to above can be produced from conventional glass-making materials properly compounded and thoroughly mixed so as to yield, when reacted, glasses of the desired composition. Suitable batch materials include glass sand, soda ash (sodium carbonate), caustic soda (sodium hydroxide), magnesite, dolomite, talc, aluminum hydrate, feldspar, aplite, nepheline syenite, zircon sand, carbon and cullet.

Besides the above-mentioned batch, melting and refining agents, such as Sb₂ O₅, As₂ O₅, Na₂ SO₄ and NaCl could also be incorporated in the glass batch. Various glass coloring agents such as compounds containing iron, cobalt, nickel, coal, silver, chromium, copper and selenium may also be added in small concentrations to the glass batch to color the final glass without impairing its desirable ion exchange properties.

For the production of glass by the updraw or float process, the well-mixed batch ingredients are fed on a continuous basis to a tank furnace to be melted and refined. The batch ingredients can be fed to the furnace as loose batch or alternately, they can be first pelletized on an inclined, rotating disc pelletizer or the like using caustic soda as a binding agent and as a total or partial replacement for soda ash. The tank furnaces for the updraw and float process are similar to most glass-making furnaces in that they are usually gas-fired and of the regenerative type well known in the art. In the updraw process, such as the Pittsburgh Process, the glass is drawn vertically upwards between rollers from the surface of a bay or drawing kiln which is located at the working end of the tank. A detailed description of the updraw process, more particularly the Pittsburgh Process may be found in Glass Manual, Pittsburgh Plate Glass Company, published in 1946. The float process for the forming of flat glass consists of floating glass sheet upon the surface of a bath of molten metal, usually tin. The float process is well known in the art and is fully described in U.S. Pat. No. 3,083,551.

After the glass has been properly melted, refined and formed as generally described above, it should have the following composition as determined by a standard wet chemical and spectrophotometric analysis:

    ______________________________________                                                     Percent by Weight                                                              on the Oxide Basis                                                 ______________________________________                                         Component     Broad Range  Preferred Range                                     ______________________________________                                         SiO.sub.2     50-58        52-57                                               Na.sub.2 O    8-23         10-19                                               K.sub.2 O     0-15         0-10                                                Na.sub.2 O + K.sub.2 O                                                                       13-25        17-23                                               Al.sub.2 O.sub.3                                                                             7-17         9-13                                                ZrO.sub.2     1-4.5        2-4.5                                               Al.sub.2 O.sub.3 + ZrO.sub.2                                                                 10-21        12-17                                               CaO           0-10         0                                                   MgO           0-6.5        4-6                                                 CaO + MgO     2.5-10       4-6                                                 TiO.sub.2     0-7          1-6                                                 TiO.sub.2 + (MgO + CaO)                                                                      4-14         5-12                                                ______________________________________                                    

With regards to the individual components, SiO₂ is the glass former and is needed to produce high temperature stability and chemical durability in the glass. Concentrations lower than the recommended amount, that is, lower than 50 percent, decrease the durability, whereas higher concentrations, that is, higher than 58 percent, require higher melting temperatures and decrease the melting rates. Sodium oxide is present as a flux to reduce the melting temperature of the glass. Also, is is present to provide the sites necessary for subsequent ion exchange. K₂ O is an optional ingredient which provides fluxing activity to the glass melt. Its presence is due usually to the use of nepheline syenite in the batch material which is a particularly desirable batch ingredient because of its cheapness and plentiful supply. Also, K₂ O is believed to increase ion exchange rates. When the K₂ O content is reduced, the reduction should be compensated for by an increase in the Na₂ O content to maintain the viscosity level. When the Na₂ O concentration is greater than the broad range specified above, that is, greater than 23 percent, the chemical durability of the glass, as measured by exposure to sulfuric acid, sodium hydroxide and water, will suffer. On the other hand, when the percentage by weight of Na₂ O or Na₂ O plus K₂ O is below the range specified, that is, below 13 percent by weight, the melting temperature of the glass will be exceedingly high. The effect of varying the K₂ O and Na₂ O contents may be seen in Table XII. With regards to the alkali metal oxides, Li₂ O has been found to decrease the rate of ion exchange and to impair the strength of the resultant chemically tempered glass article of the above compositional family, and, therefore, the glasses of the present invention should be substantially free of Li₂ O. By the expression substantially free of Li₂ O is meant that there is no purposeful addition of a lithium compound to the glass batch. Any LiO₂ which is analytically determined in the final glass is present in the impurity quantities, that is, less than 0.1 percent by weight.

Al₂ O₃ is present in the glass to promote the ion-exchange properties of the glass, such as increasing the rates of ion exchange. Also, higher Al₂ O₃ concentrations increase the strain point which results in the possibility of higher ion exchange temperatures and faster and deeper ion exchanges and penetrations. Concentrations of alumina lower than the recommended amount, that is, less than 7 percent by weight, decrease the ultimate strength obtainable in the glass, whereas higher concentrations than recommended, that is, higher than 17 percent, decrease the melting rate and result in poor acid durability. The strength of the resultant chemically tempered glass articles are dependent upon the combined total of ZrO₂ plus Al₂ O₃. However, the Al₂ O₃ plus ZrO₂ concentration should not be greater than 21 percent because of difficulty in melting. With high Al₂ O₃ plus ZrO₂ contents, the batch is not as soluble in the melt as it is with lower concentrations. Also, the Al₂ O₃ plus ZrO₂ concentration should not be below 10 percent by weight because the degree of potential strengthening in the glass will diminish to an undesirably low level.

EXAMPLES 3-9

The ZrO₂ content is essential in obtaining low temperature melting properties while maintaining credible strength and good chemical durability. To demonstrate the role of ZrO₂ in glass, this oxide was completely replaced by an equivalent amount of SiO₂ and with Al₂ O₃. The replacement with Al₂ O₃ will most nearly preserve strength, insomuch as strength was found to be dependent on the total Al₂ O₃ plus ZrO₂ content.

Tables V and VI show the effects of these replacements on strength and other various properties.

                                      Table V                                      __________________________________________________________________________     SiO.sub.2 for ZrO.sub.2 Substitution to Reduce Strength                        Component                                                                              Example 2                                                                             Example 3                                                                             Example 4                                                                             Example 5                                                                             Example 6                                  __________________________________________________________________________     SiO.sub.2                                                                              54.5   55.5   56.5   57.5   59                                         Na.sub.2 O                                                                             18.0   18.0   18.0   18.0   18.0                                       Al.sub.2 O.sub.3                                                                       10.0   10.0   10.0   10.0   10.0                                       MgO     5.0    5.0    5.0    5.0    5.0                                        K.sub.2 O                                                                              3.0    3.0    3.0    3.0    3.0                                        ZrO.sub.2                                                                              4.5    3.5    2.5    1.5    0                                          TiO.sub.2                                                                              5.0    5.0    5.0    5.0    5.0                                        Abraded Rod                                                                    MOR in psi.sup.1                                                                       65,900 52,100 49,100 41,100 36,370                                     Temperature                                                                    at 10.sup.2.0                                                                  poises ° F.                                                                     2575   2590   --     2624   2638                                       __________________________________________________________________________      1 - Ion exchange conditions - 1 hour at 1000° F. in molten              KNO.sub.3 ; MOR's 4-point loading, nominal 2 mils compressed layer.      

                                      Table VI                                     __________________________________________________________________________     Effect of ZrO.sub.2 on Strength, Melting Properties and Acid Durability                    Percent by Weight on the Oxide Basis                               Component   Example 1                                                                              Example 2                                                                              Example 7                                                                              Example 8                                                                              Example 9                          __________________________________________________________________________     SiO.sub.2   56.0    54.5    56.0    58.0    53.5                               Na.sub.2 O  18.0    18.0    18.0    16.0    17.0                               Al.sub.2 O.sub.3                                                                           12.0    10.0    16.5    16.5    11.0                               MgO         4.5     5.0     4.5     4.5     5.0                                K.sub.2 O   3.0     3.0     3.0     3.0     3.0                                ZrO.sub.2   4.5     4.5     --      --      4.5                                TiO.sub.2   2.0     5.0     2.0     2.0     6.0                                Physical Properties                                                            Temperature at                                                                 10.sup.2.0 poises                                                                          2696° F.                                                                        2575° F.                                                                        2807° F.                                                                        2924° F.                                                                        2602° F.                    Annealing Point                                                                            1070° F.                                                                        1070° F.                                                                        1067° F.                                                                        1105° F.                                                                        1094° F.                    Abraded MOR (Rods).sup.1                                                                   66,100 psi                                                                             69,900 psi                                                                             55,900 psi                                                                             --      78,300 psi                         Weight Loss in                                                                 Acid.sup.2  0.01 mg/cm.sup.2                                                                       0.01 mg/cm.sup.2                                                                       1.21 mg/cm.sup.2                                                                       0.02 mg/cm.sup.2                                                                       0.01 mg/cm.sup.2                   __________________________________________________________________________      .sup.1 - 1 hour - 1000° F. - KNO.sub.3 - Tumble abrasion; 4-point       loading, nominal 2 mils compression layer.                                     .sup.2 - Unexchanged 2 inch square boiled 30 minutes in 0.5 weight percen      H.sub.2 SO.sub.4.                                                        

From the above Tables V and VI, it is clear that the elimination of ZrO₂ is damaging in three respects: it directly raises the melting temperature, strength is decreased, and it caused a serious breakdown in resistance to attack in an acid environment. To restore acid resistance will require a substantial reduction of Na₂ O. This increases viscosity even more and leads to a viscous glass. For example, glass 8 in the above table contains 2 percent less Na₂ O than glass 7. This change caused the temperature corresponding to the viscosity at 100 poises to increase another 117° F. for a total increase of 228° F. over the corresponding temperature for glass 1. But the data presented in the above table shows that even with this increase in viscosity, the restoration of acid durability is still not complete.

Therefore, from the data in Tables V and VI it is shown that ZrO₂ plus Al₂ O₃ should not be diminished if strength is to be preserved. They also show that there must be a combination of ZrO₂ and Al₂ O₃ present to maintain high strength and good chemical durability in a low temperature melting glass. It is concluded that the ZrO₂ content should be at least 1.0, and preferably 2 to 4.5 percent by weight and ZrO₂ plus Al₂ O₃ content of 10-21, and preferably 12-17 percent by weight. The ZrO₂ component of glasses is directly responsible for lowering the melting requirements of the soda-zirconia-aluminosilicate ion exchange glasses of the present invention. The partial substitution of the ZrO₂ for Al₂ O₃ (without reducing strength) is indirectly responsible for reducing the melting requirement much more. It does this by permitting a substantial increase in the use of Na₂ O without seriously degrading acid durability. ZrO₂ is therefore important principal ingredient for a strong glass that will melt at low temperatures and will offer good resistance to attack in acid, neutral and alkaline environments.

EXAMPLES 10 - 13

Titania (TiO₂) also has a pronounced effect on melting temperature and an apparent effect on the development of strength in the chemically strengthened glasses of the invention. The following examples are presented to show the effects of TiO₂ on strength and melting properties.

                                      Table VII                                    __________________________________________________________________________     Effect of TiO.sub.2 on Strength and Melting                                    Component                                                                              Example 2                                                                             Example 10                                                                            Example 11                                                                            Example 12                                                                            Example 13                                 SiO.sub.2                                                                              54.5   55.5   56.5   57.5   53.5                                       Na.sub.2 O                                                                             18.0   18.0   18.0   18.0   18.0                                       Al.sub.2 O.sub.3                                                                       10.0   10.0   10.0   10.0   10.0                                       MgO     5.0    5.0    5.0    5.0    5.0                                        K.sub.2 O                                                                              3.0    3.0    3.0    3.0    3.0                                        ZrO.sub.2                                                                              4.5    4.5    4.5    4.5    4.5                                        TiO.sub.2                                                                              5.0    4.0    3.0    2.0    6.0                                        Temperature                                                                    at 10.sup.2.0                                                                  poises ° F.                                                                     2579   2612   2633   2667   2557                                       Annealing                                                                      Point° F.                                                                       1059   1063   1054   1054   1067                                       Abraded Rod                                                                    MOR in psi.sup.1                                                                       60,095 48,075 56,640 44,314 66,684                                     __________________________________________________________________________      .sup.1 Ion exchange conditions - 1 hour at 1000° F. in molten           KNO.sub.3 ; MOR's 4-point loading, nominal 2 mils compression layer.     

The reduction of TiO₂ from a high of 6.0 percent in Example 13 to 2 percent in Example 12 caused the melting temperature to increase about 110° F. Further, TiO₂ appears to have an effect on strength developed in chemically tempered glass. With the exception of Example 10, there is a steady increase in strength as the TiO₂ content is increased from 2 to 6 percent.

EXAMPLES 14-26

To show the effect that ZrO₂ concentrations have on the liquidus temperature and working range of ion exchange glasses, glasses having the following calculated glass compositions were made by conventional melting and forming techniques.

                                      Table VIII                                   __________________________________________________________________________     Role of ZrO.sub.2 on Working Range and Liquidus                                Component  Example 14                                                                            Example 15                                                                            Example 16                                                                            Example 17                                                                            Example 18                                                                            Example 19                                                                            Example                   __________________________________________________________________________                                                          20                        SiO.sub.2  56.75  57.0   57.25  57.5   58.0   59.0   60.0                      Na.sub.2 O 16.0   16.0   16.0   16.0   16.0   16.0   16.0                      Al.sub.2 O.sub.3                                                                          13.5   13.5   13.5   13.5   13.5   13.5   13.5                      MgO        4.5    4.5    4.5    4.5    4.5    4.5    4.5                       K.sub.2 O  3.0    3.0    3.0    3.0    3.0    3.0    3.0                       ZrO.sub.2  6.25   6.0    5.75   5.5    5.0    4.0    3.0                       Temperature at                                                                 10.sup.2.0 poises, ° F.                                                            --     2848   --     --     2875   2896   2911                      Temperature at                                                                 10.sup.4.0 poises, ° F.                                                            ≃2134                                                                   2134   ≃2134                                                                   ≃2134                                                                   2138   2139   2139                      Liquidus                                                                       Temperature, ° F.                                                                  2336   2240   2240   2146   NCD*   NCD*   NCD*                      Working Range, ° F.                                                                -202   -106   -106   -12    >125   >125   >125                      __________________________________________________________________________     Component  Example 21                                                                            Example 22                                                                            Example 23                                                                            Example 24                                                                            Example 25                                                                            Example 1                                                                             Example                   __________________________________________________________________________                                                          26                        SiO.sub.2  61.0   54.5   54.5   55.0   55.5   56.0   56.5                      Na.sub.2 O 16.0   18.0   18.0   18.0   18.0   18.0   18.0                      Al.sub.2 O.sub.3                                                                          13.5   12.0   12.0   12.0   12.0   12.0   12.0                      MgO        4.5    3.5    4.5    4.5    4.5    4.5    4.5                       K.sub.2 O  3.0    3.0    3.0    3.0    3.0    3.0    3.0                       ZrO.sub.2  2.0    7.0    6.0    5.5    5.0    4.5    4.0                       TiO.sub.2  --     2.0    2.0    2.0    2.0    2.0    2.0                       Temperature at                                                                 10.sup.2.0 poises, ° F.                                                            2934   2697   2687   2677   2697   2696   2722                      Temperature at                                                                 10.sup.4.0 poises, ° F.                                                            2136   2015   1998   1984   1990   1981   2002                      Liquidus                                                                       Temperature, ° F.                                                                  NCD*   2050   1996   1944   1926   NCD*   NCD*                      Working Range, ° F.                                                                >125   -35    2      40     64     >125   >125                      __________________________________________________________________________       *No crystals determined.                                                

The above experiments show that when ZrO₂ is maintained below 5 percent by weight, within the range of 2 to 4.5 percent by weight, devitrification generally occurs so slowly that it is difficult to detect any evidence of devitrification under the conditions given. On the other hand, glass compositions containing greater than 5 percent by weight ZrO₂ have narrow working ranges and may even have liquidus temperatures above the forming temperatures, resulting in a negative working range and could pose a serious problem with respect to float or updraw forming.

It should be mentioned at this point where it is stated in the specification and claims that the glass compositions of the present invention have working ranges greater than 125° F. what is meant is that no detectable crystals developed when the glass was heated for at least 66 hours at a temperature range extending from above the temperature corresponding to 10⁴.0 poises to at least 125° F. below such temperature. The method for determining liquidus temperatures and for detecting crystals is as described above. That is, small platinum packets are filled with glass crushed in a hardened steel mortar and the packets positioned in sand along the temperature gradient of a gradient wound tube furnace. After a soak period of at least 66 hours, the packets are removed and quenched in water. The contents of each packet are then examined for the presence of crystals in the following manner. The fused glass is powdered in an agate mortar and a portion of the powder is placed on a microscope slide, along with a drop or two of oil with an index of refraction close to that of the glass. The submerged glass particles are then viewed with a microscope at 100X to 200X between crossed polarizers. In the absence of crystals, the field remains dark. Birefringent crystals will rotate the plane of polarization of the light coming through the first polarizer and thus appear as bright areas in the dark field.

EXAMPLES 27-29

MgO and CaO are employed as fluxes to decrease the melting temperature. Preferably, MgO is the total source of alkaline earth metal oxide in the glass batch. MgO provides for enhanced strength in the resultant chemically strengthened article. Strength is decreased somewhat if CaO is substituted for MgO as Table IX below shows.

                                      Table IX                                     __________________________________________________________________________     Component                                                                              Example 2                                                                             Example 27                                                                            Example 28                                                                            Example 29                                        __________________________________________________________________________     SiO.sub.2                                                                              54.5   54.5   54.5   54.5                                              Na.sub.2 O                                                                             18.0   18.0   18.0   18.0                                              Al.sub.2 O.sub.3                                                                       10.0   10.0   10.0   10.0                                              MgO     5.0    3.5    2.0    0                                                 K.sub.2 O                                                                              3.0    3.0    3.0    3.0                                               ZrO.sub.2                                                                              4.5    4.5    4.5    4.5                                               TiO.sub.2                                                                              5.0    5.0    5.0    5.0                                               CaO     0      1.5    3.0    5                                                  ##STR1##                                                                               0      0.3    0.6    1.0                                              Abraded Rod                                                                    MOR.sup.1 (psi)                                                                        65,200 61,400 48,200 45,100                                            __________________________________________________________________________       .sup.1 All rods exchanged for 1 hour in KNO.sub.3 at 1000° F.          test; 4-point loading.                                                   

From the above table, it can be seen that the glasses representing substitutions for MgO all contain 5 percent alkaline earth metal oxide (MgO plus CaO). It is evident from the data in the above table that as CaO replaces MgO, there is a decrease in strength. The decrease is a maximum when the replacement is complete. Even in this instance, however, strength would appear to remain adequate for most potential uses. CaO is shown to be a somewhat better flux than MgO, insomuch as high temperature viscosity decreases with its substitution for MgO, and acid durability remains unchanged. The working range in most instances will be adequate for updraw as well as for float forming. In addition, the simple substitution of CaO for MgO on a partial or total basis offers a means of controlling the strength of the glass in the manufacturing stage. With regards to the total MgO plus CaO content, higher than recommended contents, that is, higher than 10 percent by weight, result in slow penetration of the strengthening ions, and contents lower than 2.5 percent by weight result in viscous high melting glasses.

As has been mentioned above, TiO₂ is a preferred component because it assists in obtaining low temperature melting properties while maintaining credible strength and good chemical durability. However, in certain applications, it might be desirable to reduce or eliminate TiO₂ in order to reduce batch costs or when introducing iron into the glass to make and infrared radiation absorbing glass for ion exchange purposes. To compensate for the viscosity increases that accompany the reduction or elimination of TiO₂, one or more of the fluxing components of the glass should be increased.

Besides the above-mentioned components, the final glass composition can also contain minor amounts, that is, less than 1 percent by weight of various oxides and anions such as As₂ O₅, Sb₂ O₅, SO₄.sup.⁻² and Cl⁻ which result from the incorporation of melting and fining agents in the glass batch materials. Coloring agents in the form of transition metal oxides, such as iron, nickel and cobalt oxides in concentrations on the order of 5 percent or less can also be present in the final glass composition. Higher concentrations, that is, on the order of 5 percent, are used when a densely colored glass is desired. Lower concentrations, i.e., on the order of 1 percent or less, are used for higher visible light transmittance glasses. Table X below lists various glass compositions which contain coloring metal oxides and which are suitable for tinted spectacle lenses and architectural applications.

                  Table X                                                          ______________________________________                                         Component  Example 30 Example 31  Example 32                                   ______________________________________                                         SiO.sub.2  54.5       53.6        49.5                                         Na.sub.2 O 18.0       18.0        18.0                                         Al.sub.2 O.sub.3                                                                          10.0       10.0        10.0                                         MgO        5.0        5.0         5.0                                          K.sub.2 O  3.0        3.0         3.0                                          ZrO.sub.2  4.5        4.5         4.5                                          TiO.sub.2  5.0        5.0         5.0                                          CoO        0.011      0.011       --                                           NiO        0.063      0.063       --                                           Fe.sub.2 O.sub.3                                                                          --         0.8         5.0                                          Shade      neutral    olive green rose smoke                                   % Luminous                                                                     Transmittance                                                                  (Illuminant C)                                                                 0.079 inch 58.2 percent                                                                              49.8 percent                                                                               14.3 percent                                 0.250 inch 21.8 percent                                                                              13.5 percent                                                                               --                                           ______________________________________                                    

The chemical strengthening treatment presently used for imparting the necessary impact resistance to conventional crown spectacle lenses (e.g., a glass having the following analyzed composition: SiO₂, 67.42 percent; Al₂ O₃, 1.98 percent; Na₂ O, 8.45 percent; K₂ O, 8.80 percent; CaO, 9.09 percent; ZnO, 2.90 percent; TiO₂, 0.34 percent; Sb₂ O₅, 1.02 percent) consists of a 16-hour soak in KNO₃ at 470° C. (878° F.). This treatment produces a compression layer on the surface of this glass that is about 2 mils thick. A compression layer of the same thickness, but with a considerably higher stress level, can be produced in the above three types of glasses (Examples 30-32) in only one hour or less.

Besides the reduced strengthening time and higher surface stress values, the above glasses offer other advantages over many conventional crown spectacle glass compositions in that the above glasses are essentially non-devitrifiable. These latter characteristics make the glass particularly compatible and especially suitable for conventional melting and pressing operations or for any method of producing ophthalmic glass blanks or glass sheets. The following tabulation compares some of the properties of the above three glass compositions to the corresponding properties of a conventional ophthalmic crown glass such as the one mentioned above.

                  Table XI                                                         ______________________________________                                                          Conventional                                                                   Ophthalmic                                                                              Glasses of                                                            Crown Glass                                                                             Example 30*                                          ______________________________________                                         Temperature at 10.sup.2.0 poises                                                                  2667° F.                                                                           2583° F.                                  Temperature at 10.sup.4.0 poises                                                                  1888° F.                                                                           1899° F.                                  Annealing Point    1026° F.                                                                           1068° F.                                  KNO.sub.3 Exchange Bath Temperature                                                               900° F.                                                                            1000° F.                                  Exchange Time for 2 mil                                                        compression layer  16 hours   1 hour                                           Average abraded modulus                                                        of rupture (Rods)  35,800 psi 67,800 psi                                       (Tumble abrasion)                                                              ______________________________________                                           *Properties for Glasses 31 and 32 would be comparable.                  

The tinted glass compositions of the present invention are not restricted to exchange treatment time and temperatures as cited above. Alternate exchange treatments that will produce a nominal 2 mil compression layer on these glasses are shown in the following tabulation, together with the average tumble abraded modulus of rupture (MOR) values for rods of glass.

    __________________________________________________________________________               Glass of Example 31*                                                 KNO.sub.3 Temperature                                                                      Exchange Time                                                                            Average Abraded MOR**                                    __________________________________________________________________________     1050° F.                                                                          1/2 hour    49,000 psi                                               1000° F.                                                                          1 hour      64,800 psi                                                950° F.                                                                          2 hours     76,200 psi                                                900° F.                                                                          4 hours     87,800 psi                                               __________________________________________________________________________       *Comparable results obtainable with Glasses 30 and 32.                         **Tumble abrasion                                                       

Other optional ingredients such as ZnO, SrO, PbO, P₂ O₅ and BaO can be present in the final glass composition in concentrations of up to 2 percent by weight. The total amount of optional ingredients, that is, the total amount of melting and fining agents, transition metal oxides and other optional ingredients such as those mentioned immediately above, in total, should constitute no more than 5 percent by weight of the final glass composition.

Examples 33 through 43 set forth in Table XII illustrate additional ion exchange glass compositions falling within the scope of the present invention, and show the effect of varying the total Na₂ O + K₂ O content and the Na₂ O to K₂ O ratio of the glass.

The alkali metal exchange strengthening treatments contemplated by the present invention are achieved by contacting the surface of the base glass with an alkali metal salt having an atomic diameter larger than sodium at an elevated temperature and for a period of time long enough to obtain a substantial exchange for the larger atomic diameter alkali metal for sodium and other exchangeable alkali or other metals in the base glass having atomic diameters smaller than the alkali metal employed for strengthening.

The alkali metal strengthening treatment is usually conducted at temperatures around the strain point of the base glass, that is, with glass of the invention, about 925°-1050° F. for a sufficient period of time to replace to a marked extent the sodium and other available smaller atomic diameter metal or metals by the larger atomic diameter alkali metal or metals of the treating salt. When highest ultimate strengths are desired, the treatment temperature is usually below the strain point, i.e., 25° to 150° F. below the strain point. Where lower strengths are adequate and speed of operation is important, the treatment may be conducted at temperatures slightly above the strain point of the glass, that is, about 25° to 100° F. above the strain point, if the treatment is conducted quickly so as not to relax excessively the compressive stresses induced in the surface of the glass by the ion exchange.

                                      TABLE XII                                    __________________________________________________________________________     Component Example 33                                                                            Example 34                                                                            Example 35                                                                            Example 36                                                                            Example 37                                                                            Example 38                                                                            Example                    __________________________________________________________________________                                                         39                         SiO.sub.2 57.5   54.5   54.5   54.5   54.5   50.5   50.5                       Na.sub.2 O                                                                               18.0   21.0   15.0   12.0   9.0    23.0   20.0                       K.sub.2 O --     --     6.0    9.0    12.0   --     3.0                        Al.sub.2 O.sub.3                                                                         10.0   10.0   12.0   12.0   10.0   12.0   12.0                       ZrO.sub.2 4.5    4.5    4.5    4.5    4.5    4.5    4.5                        MgO       5.0    5.0    5.0    5.0    5.0    5.0    5.0                        TiO.sub.2 5.0    5.0    5.0    5.0    5.0    5.0    5.0                        Annealing Point                                                                ° F.                                                                              1109   1067   1075   1082   1112   1054   1049                       Temp. at 100                                                                   poises, ° F.                                                                      2674   2534   2647   2718   2789   2471   2576                       Temp. at 10,000                                                                poises, ° F.                                                                      1966   1867   1947   2002   2066   1832   1859                       Compression layer                                                              depth, mils*                                                                             1.4    2.0    2.2    2.6    2.8    2.3    2.6                        Compression layer                                                              depth, mils**                                                                            1.4    1.9    2.5    3.1    3.3    2.3    2.5                        Abraded rod MOR,                                                               psi*      59,400 35,900 56,100 61,900 51,300 26,500 47,100                     Abraded rod MOR,                                                               psi**     70,200 69,000 77,800 66,700 56,200 66,000 75,800                     __________________________________________________________________________     Component Example 40                                                                            Example 41                                                                            Example 42                                                                             Example 43                                     __________________________________________________________________________     SiO.sub.2 50.5   50.5   50.5   50.5                                            Na.sub.2 O                                                                               16.0   13.0   10.0   18.0                                            K.sub.2 O 7.0    10.0   13.0   7.0                                             Al.sub.2 O.sub.3                                                                         10.0   10.0   10.0   12.0                                            ZrO.sub.2 4.5    4.5    4.5    4.5                                             MgO       5.0    5.0    5.0    5.0                                             TiO.sub.2 5.0    5.0    5.0    5.0                                             Annealing Point                                                                ° F.                                                                              1060   1076   1101   1011                                            Temp. at 100                                                                   poises, ° F.                                                                      2589   2651   2724   2488                                            Temp. at 10,000                                                                poises, ° F.                                                                      1912   1966   2032   1830                                            Compression layer                                                              depth, mils*                                                                             2.7    3.1    3.4    3.2                                             Compression layer                                                              depth, mils**                                                                            2.7    3.3    3.7    3.4                                             Abraded rod MOR,                                                               psi*      55,500 58,900 53,000 24,800                                          Abraded rod MOR,                                                               psi**     77,400 77,900 56,100 63,400                                          __________________________________________________________________________      *Ion exchanged 1 hr. at 1000° F. in molten KNO.sub.3                    **Ion exchanged 4 hrs. at 900° F. in molten KNO.sub.3             

The length of the treatment period depends upon several factors including, among others, the specific composition of the base glass, the relative rate of exchange of a given larger atomic diameter alkali metal, and the specific treatment temperature. The temperature period can range from short contact periods of about several minutes up to a period of 100 hours. However, for treatment temperatures in excess of about 850° F. and ranging from about 900° F. to 1025° F., contact periods of about 10 minutes to 50 hours are usually sufficient depending on the thickness of the compression layer desired. In fact, when higher treatment temperatures are used, that is, 1050° to 1100° F., the base glass compositions can be provided with greatly enhanced surface compressive stresses and load strengths by treatment times ranging from 8 minutes to 2 hours depending on the thickness of the compression layer desired. Longer periods of contact are not objectionable to obtain a given set of objectives so long as the surface compressive strength and the load strength induced by the alkali metal strengthening treatment is substantially retained over the entire treatment period at the treatment temperatures employed.

The results of the larger atomic diameter alkali metal strengthening treatment is to deplete the sodium content on the surface and thereby generate a surface which is in compression for a specified depth of penetration and is rich in the larger atomic diameter alkali metal, for example, potassium, cesium and rubidium, of the alkali metal treating salt employed for strengthening. When potassium is employed as the larger atomic diameter alkali metal, the penetration of potassium into the surface of the treated glass usually takes place to a depth of about 25 to 250 microns, although other depths are obtainable by varying the ion exchange process parameters, as is known in the art.

The potassium metal salt causes the imposition of enhanced surface compressive stress to a greater depth than obtainable when using cesium or rubidium salts. Also, as between potassium, cesium and rubidium, potassium strengthening salts are more readily available and hence less expensive.

The alkali metal salt strengthening treatment is conducted conveniently by immersing the base glass into a molten bath of the larger atomic diameter alkali metal strengthening salt for a sufficient period of time to secure the desired exchange and penetration of the larger atomic diameter alkali metal into the surface of the base glass. To effect this treatment, the alkali metal strengthening salt is placed in a suitable container, for example, stainless steel tanks, or other inert receptacle, and heated to a temperature at which it is molten. Usually the temperature of treatment will vary between the threshold temperature at which the alkali metal treating salt becomes molten and a temperature around the strain point of the base glass being strengthened, and any convenient treating temperature between the melting point of the alkali metal strengthening salt and the temperature at the glass strain point or slightly above can be used.

Prior to immersion of the base glass into the molten alkali metal salt treatment bath, the base glass article is preferably heated to a temperature within the range of 50° F. above or below the temperature at which the alkali metal exchange treatment is to be conducted, that is, the temperature at which the alkali metal salt is maintained during treatment. More preferably, the glass article is preheated to a temperature fairly close approximating that at which the exchange strengthening treatment is conducted.

In a typical method of performing this invention, the preheated base glass in sheet form is dipped into a molten bath of potassium nitrate maintained at a temperature of about 800° to 1100° F. and treated for a period of about 8 minutes to about 100 hours. This strengthening treatment causes introduction of potassium into the surface of the base glass by replacement of potassium for the sodium and other exchangeable smaller atomic diameter metals or other electropositive elements in the surface of the base glass at the time of treatment, thereby developing high surface compressive stress and load strength in the glass and depleting the sodium content at the surface.

The treated glass article is then removed from the molten potassium nitrate treating bath and cooled gradually to a temperature roughly approximating room temperature, that is, a temperature ranging from 200° F. down to and even below room temperature. Following cooling, the glass is usually subjected to aqueous rinsing to remove excess treating salt.

Instead of a potassium treating salt, a molten cesium or rubidium salt, for example, rubidium or cesium nitrate, can be employed for strengthening the base glass. In such a case, the rubidium and cesium from the treating salt exchanges for the sodium and potassium, each being a smaller atomic diameter alkali metal than rubidium and cesium, thereby incorporating rubidium or cesium into the surface of the base glass to produce rubidium or cesium exchange strengthened glass. Obviously, mixed salt ion exchange treating baths could be used such as mixed molten potassium and cesium salt baths.

The alkali metal salt used for the strengthening treatment should be fairly stable at the treatment temperatures employed. Typically, satisfactory salts are those of the mineral acids, such as sulfates, nitrates, chlorides, fluorides and phosphates of potassium, cesium and rubidium, which are low in alkalinity and do not seriously deface or etch the base glass article.

The foregoing discussion has related to employing a single larger atomic diameter alkali metal exchange strengthening treatment, and for most purposes, a single exchange treatment is widely satisfactory to secure the desired results. However, it is also within the purview of this invention to strengthen the SiO₂ --Na₂ O--Al₂ O₃ --alkaline earth metal oxide-ZrO₂ glass by subjecting it to a series of alkali metal salt exchange treatments. In such similarly conducted experiments, each successive treatment is conducted using an alkali metal salt having a larger atomic diameter than the alkali metal employed for a prior exchange strengthening treatment. Such successive later exchange treatment or treatments, all of which are preferably conducted at temperatures below the glass strain point, can serve to increase the magnitude of surface compressive stress and even thickness of the surface compressive stress zone.

For example, the base glass can be subjected first to potassium exchange strengthening treatment, using molten potassium nitrate treating salts, followed by a further alkali metal strengthening treatment using a molten salt of an alkali metal having an atomic diameter larger than potassium, for example, a molten rubidium salt, such as molten rubidium nitrate. The effect of the second alkali metal strengthening treatment is to deplete the potassium and other available exchangeable lower atomic diameter alkali metals at the surface of the glass, thus replacing them with rubidium. By this means the magnitude of the compressive stress at the surface of the glass and hence its load strength can be increased. Moreover, if desired, the sodium-potassium exchange strengthened glass can be subjected to further successive alkali metal exchange treatments using first rubidium and then a cesium salt, respectively.

Usually when strengthening the base glass compositions by the use of such successive alkali metal salts exchange strengthening treatments, the glass is cooled between each exchange treatment to a temperature ranging from 200° F. down to and even below room temperature. Following cooling, the glass is usually subjected to aqueous rinsing or to other cleansing prior to subsequent exchange treatments to remove excess treating salts. The glass is then preheated prior to a subsequent exchange treatment or treatments.

However, it is also within the purview of the present invention to avoid the loss in time and thermal energy required in cooling the glass to room temperature between exchange treatments, and then preheating the glass to temperatures approximating those at which the subsequent exchange treatment or treatments are to be conducted, by cleansing the glass without first cooling to room temperature by impinging the flowing preheated air or other inert gases (which have been preheated to the treatment temperature to be employed in the subsequent exchange treatment) upon a surface of the treated glass, thereby serving to remove excess molten treating salts. Instead of gases, absorbing clays or silica powders can be employed for high temperature cleansing and these materials can serve to absorb excess molten salt.

While the various above-mentioned exchange strengthening treatments can be conducted effectively by immersion of the base glass in a molten salt of a larger atomic diameter alkali metal salt, other methods of contact can be used. For example, the base glass can be sprayed or otherwise provided with an adhering coating of the potassium and the coated glass can be heated to a temperature at which the potassium salt is molten to effect a non-immersion exchange strengthening.

Furthermore, the alkali metal treating salt can be mixed with a coherent, inert carrier or diluent, for example, thixotropic clay, to form a paste which is adherent to the glass and the paste, then applied to the glass prior to or simultaneously with or even shortly after heating the glass to treatment temperatures. The paste should usually contain from about 15 to 80 percent by weight of alkali metal salt to achieve non-immersion exchange strengthening within reasonably rapid treating periods.

The present invention can be employed to produce strengthened glass articles of all types, for example, sheet, wind screens, automobile windshields, side windows and back windows, building materials, architectural glass or spandrels, skylights, bottles, plates, casseroles, saucers, cups, bowls and other tableware, drinking glasses and goblets, viewing closures, such as window panes and glass doors, safety glass and other laminated viewing closures and structures, glass insulation structures wherein a plurality of glass sheets are arranged in spaced fashion with a layer of air or fluorocarbon serving as the insulation medium, television safety glass implosion and/or explosion shields, ophthalmic lenses for eye glasses, goggles, etc., glass roofs or transparent domes in vehicles and buildings, and experimental devices such as glass engine parts. 

I claim:
 1. In a method for strengthening an alkali metal silicate glass article in which sodium ions in the surface of the glass article are replaced by larger monovalent alkali metal ions by bringing the surface of the glass article into contact with the source of said larger monovalent alkali metal ions so as to place a compression layer in the surface of the glass article, the improvement which comprises forming the article to be strengthened from an alkali metal oxide-zirconia-aluminosilicate glass consisting essentially by weight on the oxide basis of about:

    ______________________________________                                         Component          Percent by Weight                                           ______________________________________                                         SiO.sub.2          [50-58] 52-57                                               Na.sub.2 O         [8-23] 10-19                                                K.sub.2 O          [0-15] 0-10                                                 Na.sub.2 O + K.sub.2 O                                                                            [13-25] 17-23                                               Al.sub.2 O.sub.3   [7-17] 9-13                                                 ZrO.sub.2          [1-4.5] 2-4.5                                               Al.sub.2 O.sub.3 + ZrO.sub.2                                                                      [10-21] 12-17                                               [CaO]              [0-10]                                                      MgO                [0-6.5] 4-6                                                 [CaO + MgO]        [2.5-10]                                                    TiO.sub.2          [0-7] 1-6                                                   [TiO.sub.2 + (MgO + CaO)]                                                                         [4-14]                                                      ______________________________________                                    

wherein the glass includes less than 0.1 percent by weight Li₂ O and the above components constitute at least 95 percent by weight of the glass composition and are proportioned relative to one another so as to provide glass having a viscosity of 100 poises at a temperature less than 2800° F. and a viscosity of 10,000 poises at a temperature less than 2050° F. and having a working range of at least 125° F.
 2. A chemically strengthened glass article exhibiting a surface compressive stress after being subjected to surface abrasion composed of an interior portion which is in tension and a surface compressive layer, said interior portion comprising a base glass consisting essentially by weight on the oxide basis of about:

    ______________________________________                                         Component          Percent by Weight                                           ______________________________________                                         SiO.sub.2          [50-58] 52-57                                               Na.sub.2 O         [8-23] 10-19                                                K.sub.2 O          [0-15] 0-10                                                 Na.sub.2 O + K.sub.2 O                                                                            [13-25] 17-23                                               Al.sub.2 O.sub.3   [7-17] 9-13                                                 ZrO.sub.2          [1-4.5] 2-4.5                                               Al.sub.2 O.sub.3 + ZrO.sub.2                                                                      [10-21] 12-17                                               [CaO]              [0-10]                                                      MgO                [0-6.5] 4-6                                                 [CaO + MgO]        [2.5-10]                                                    TiO.sub.2          [0-7] 1-6                                                   [TiO.sub.2 + (MgO + CaO)]                                                                         [4-14]                                                      ______________________________________                                    

wherein the glass includes less than 0.1 percent by weight Li₂ O and the above components constitute at least 95 percent by weight of the base glass composition and are proportioned relative to one another so as to provide a base glass having a viscosity of 100 poises at a temperature less than 2800° F. and a viscosity of 10,000 poises at a temperature less than 2050° F., and having a working range of at least 125° F.; said surface layer having a composition chemically altered from that of the base glass to the extent that the surface layer has a lesser content of sodium with a correspondingly greater content on an ionic basis of a monovalent alkali metal ion having a larger ionic diameter than sodium. 